预铺自粘型防水卷材技术要求论文发表代理

 

　　关键词：预铺自粘型防水卷材；地下铁道工程；物理性能

 

　　Pre applied self-adhesive waterproof membrane and the technical requirements of the underground railway engineering

 

　　Abstract: The characteristics of Pre-applied self-adhesive waterproof sheets were analyzed, and some issues about its application in Metro project were discussed combining with construction features. Shopped for the pre-self-adhesive waterproof membrane construction problems, to the experimental data on the quality control of products, there are still difficulties, companies should first focus the main production processes, improved production processes and improved formulation in order to ensured that products meet the design in use requirements.

 

　　Key words: Pre-applied self-adhesive waterproof sheets; Metro project; Physical Properties

 

　　中图分类号；E924.95      文献标识码：A         文章编号：

 

　　1 前言

 

　　预铺自粘型防水卷材根据目前市面上的产品类型主要可分为三大类：双面自粘型沥青基聚酯胎预铺防水卷材、高密度聚乙烯自粘胶膜防水卷材和三元乙丙橡胶反应型防水卷材。轨道交通地下工程大多采用围护桩或地下连续墙支护的结构型式，其铺设防水层时，结构底板均采用“外防内贴”法，顶板均采用“外防外贴”法，侧墙大多采用“外防内贴”法，局部采用放坡施工的侧墙采用“外防外贴”法。在侧墙和底板柔性防水材料中，由于预铺防水卷材具有不易窜水和施工简便的特点，在地铁工程中得到越来越广泛的应用。

 

　　2自粘型防水卷材应用优势:

 

　　自粘卷材具有以下优点：首先，它们符合现在安全、环保的要求。这类卷材在使用时无需加热，没有异味，使用安全；没有挥发性有机物质，对环境友好。

 

　　改性沥青卷材在发达国家已经使用了几十年。现在的技术已经发展到使用时不需要明火和加热，而是采用冷粘法施工，即自粘卷材技术。该技术在我国也得到大力的推广和应用。因为自粘卷材要求在10 ℃时必须能粘，而一般的SBS 混合物在环境温度下粘结力较小，所以在低温时它不适合作为自粘卷材。在过去，这一点限制了自粘卷材的应用。近年来，技术不断发展进步，自粘卷材已有这种现实，在低温情况下也可施工自粘卷材不像冷粘剂那样需要固化时间。自粘卷材可以直接用在处理过的基面上，立即就能达到初始的剥离强度，在环境温度下就能防水。通常在空气、阳光或其他外界的加热作用下，几天后搭接处就会达到最大的剥离强度。

 

　　自粘卷材的另一个优点就是使用方便。它不需要特殊的设备；与其它许多传统防水卷材相比，劳动强度较小。施工步骤简单：将卷材在处理好的基面上铺开；稍后，撕去隔离膜，卷材就粘牢在基面上；接下来按照同样的方法铺设，端部搭接和接缝处按照生产商的要求施工。预铺反粘防水卷材应用施工时更简单：空铺于基层上，做好临时固定和接缝处理就完成铺设。

 

　　自粘防水卷材方法的另一大优势是它提供了更均一的施工速度，消除了粘结性不足或胶粘剂不够的问题，并减少了相关的风干性问题。因为不需要相关的粘结固化时间，自粘施工方法劳动强度较小、施工速度快。最近有生产商做过试验对比：该方法最多比胶带接缝法快50倍，比水基粘结剂快5倍，比油基粘结剂快3倍。

 

　　3南京地铁三号线、十号线自粘型防水卷材技术标准及检测数据及分析

 

　　表1

 

　　4mm厚双面自粘型沥青基聚酯胎预铺防水卷材序号检 测 项 目指 标样品编号（12组样品）

 

　　123456

 

　　1单位面积重量， kg/㎡   ≥4.1 4.74.84.64.74.54.7

 

　　2厚度mm平均值≥4.0 4.24.24.24.14.24.1

 

　　最小单值≥3.7 4.24.14.14.0 4.0 4.0

 

　　3 可溶物含量，g/㎡   ≥2900 306735112943333930793625

 

　　4拉伸性能拉力，N/50mm≥纵向800 98884310791042983967

 

　　横向847812946945843885

 

　　最大拉力时伸长率，％≥纵向40 614857564757

 

　　横向796181835984

 

　　5 钉杆撕裂强度，N  ≥纵向200 250310387364357276

 

　　横向255303382348337276

 

　　6冲击性能，直径（10±0.1)mm无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏

 

　　7静态荷载，20kg无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏

 

　　8耐热性，70℃，2h无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落

 

　　9低温柔性-25℃无裂纹-25℃无裂纹-25℃无裂纹-25℃无裂纹10个试件均有裂纹-25℃无裂纹-25℃无裂纹

 

　　10渗油性，张数 ≤2 1 1 1 1 1 1

 

　　11与后浇混凝土剥离强度，N/mm ≥无处理2.0 1.12.61.02.80.90.7

 

　　水泥粉污染表面1.5 0.91.70.62.70.40.6

 

　　泥沙污染表面1.5 1.63.21.23.20.50.9

 

　　紫外线老化1.5 0.82.70.80.62.63.0

 

　　热老化1.5 2.63.91.52.61.20.7

 

　　12热老化（70℃，168h）拉力保持率，％ ≥纵向　989397979495

 

　　横向90 999397939295

 

　　伸长率保持率，％ ≥纵向　919097999491

 

　　横向80 96 95 94 91 88 89

 

　　低温柔性 -23℃，无裂纹 -23℃，无裂纹 -23℃，无裂纹 -23℃，无裂纹10个试件均有裂纹 -23℃，无裂纹 -23℃，无裂纹

 

　　13热稳定性外观无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌

 

　　尺寸变化，％ ≤纵向2.0 0.50.40.40.40.40.4

 

　　横向0.40.40.30.40.40.4

 

　　判定不合格合格不合格不合格不合格不合格

 

　　表1续  12组4mm厚双面自粘型沥青基聚酯胎预铺防水卷材检测数据汇总

 

　　4mm厚双面自粘型沥青基聚酯胎预铺防水卷材序号检 测 项 目指 标样品编号（12组样品）

 

　　789101112

 

　　1单位面积重量， kg/㎡   ≥4.1 4.54.64.84.74.74.6

 

　　2厚度mm平均值≥4.0 4.24.24.24.14.0 4.2

 

　　最小单值≥3.7 4.1 4.1 4.1 4.0 3.9 4.2

 

　　3 可溶物含量，g/㎡   ≥2900 327736433116291834223064

 

　　4拉伸性能拉力，N/50mm≥纵向800 885114087396712141148

 

　　横向80910018379209721055

 

　　最大拉力时伸长率，％≥纵向40 465049515662

 

　　横向665354578887

 

　　5 钉杆撕裂强度，N  ≥纵向200 297304308307264278

 

　　横向284302313304248266

 

　　6冲击性能，直径（10±0.1)mm无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏

 

　　7静态荷载，20kg无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏无渗漏

 

　　8耐热性，70℃，2h有流淌、滴落有流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落无位移、流淌、滴落

 

　　9低温柔性-25℃无裂纹10个试件均有裂纹-25℃无裂纹-25℃无裂纹-25℃无裂纹-25℃无裂纹-25℃无裂纹

 

　　10渗油性，张数 ≤2 1 1 1 1 1 1

 

　　11与后浇混凝土剥离强度，N/mm ≥无处理2.0 3.11.0 0.82.0 2.30.8

 

　　水泥粉污染表面1.5 2.00.70.70.62.30.4

 

　　泥沙污染表面1.5 3.80.90.71.52.20.9

 

　　紫外线老化1.5 2.00.60.40.90.90.4

 

　　热老化1.5 3.41.51.0 2.42.60.5

 

　　12热老化（70℃，168h）拉力保持率，％ ≥纵向93　979493929692

 

　　横向90 969890929895

 

　　伸长率保持率，％ ≥纵向84　938788859687

 

　　横向80 90 94 89 86 93 97

 

　　低温柔性 -23℃，无裂纹10个试件均有裂纹 -23℃，无裂纹 -23℃，无裂纹 -23℃，无裂纹 -23℃，无裂纹 -23℃，无裂纹

 

　　13热稳定性外观无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌无起皱、滑动、流淌

 

　　尺寸变化，％ ≤纵向2.0 0.40.40.40.30.40.3

 

　　横向0.40.40.50.40.40.4

 

　　判定不合格不合格不合格不合格不合格不合格

 

　　数据分析：4mm厚双面自粘型沥青基聚酯胎预铺防水卷材12家企业提供的12组样品，其中合格1家，不合格11家。其中低温柔性（-25℃）2个样品不合格，不合格率17%；与后浇混凝土剥离强度10个样品不合格，不合格率83%；热老化后低温柔性（-23℃）2个样品不合格，不合格率17%；耐热性（70℃，2h ）2个样品不合格，不合格率17%。

 

　　从数据分析，样品的拉伸性能合格率较高，体现了产品抗拉强度高、并具较大延伸率，对基层伸缩或开裂变形的适应性强；可形成高强度防水层，对压力水抵抗能力强的特点。不合格项目主要集中在“与后浇混凝土剥离强度”项目上，强度值比标准要求低20%～50%。虽然产品的优势在于粘结性能好，并具有自愈功能，卷材与基层满粘接，接缝自身粘接与卷材同寿命，但是由于生产工艺的问题造成了产品先天不足，反而不能发挥产品性能的优势。

 

　　4结论

 

　　实验室试验数据充分说明的预铺防水卷材任有以下的缺点：1）低温施工时搭接缝粘贴质量不易保证；2）高温环境施工时，易出现流淌现象；3）产品粘贴质量受配方影响较大，遇水遇污染不易粘贴。4）耐久性老化性能存在争论。

 

　　预铺自粘型防水卷材虽然已经成为我国基础建设特别是城市轨道交通建设的主流产品，代替了传统的需要明火加热连接的沥青基防水卷材，但是在实际使用中，产品的质量残差不齐，实验室检测通过率不高，通过企业出厂检验的合格品的性能仍不稳定。在现场施工使用中，效果也不是很理想，粘结处漏水现象时有发生，实验室检测与后浇混凝土的剥离强度很低，也反映了这一现象。因此，在总结上述实验结果后，厂家应不断总结经验，按照检测结果反映出的质量问题，攻克对材料配方、生产工艺的难点，达到实验室技术指标，才能在施工应用中占领更广阔的市场。

 

　　参考文献

 

　　[1] 郭德友.预铺防水卷材应用技术探讨[J].中国建筑防水,2010(21):1-4.

 

　　[2] 何克文.地铁天津站交通枢纽工程地下结构新型防水材料应用技术[J].新型建筑材料,2010(21):41-44.

 

　　[3] 蒋雅君.自粘防水卷材在隧道防水中得适应性探讨[J].新型建筑材料,2007(2):69-72.

 

　　[4] 扬州市建筑勘查设计院. 造工程可行性研究报告[R].2008.